Electronics Forum | Wed Dec 11 11:35:15 EST 2019 | dilogic
Just out of curiosity - what is the rationale behind specifying mask thicknes?
Electronics Forum | Wed Dec 11 13:00:07 EST 2019 | slthomas
Excessive mask thickness also can wreak havoc on stencil printing.
Electronics Forum | Wed Oct 13 12:07:43 EDT 1999 | mikeh
Hi, I am currently using a peelable mask prior to wave soldering and have started exploring water soluble/washable masks. The mask will be used with water based and alcohol based flux. Are there any compatability issues to concider and how will this
Electronics Forum | Wed Nov 20 01:38:53 EST 2019 | ajspec
Hi, i'm facing solder mask peel off but limited to the solder defined pad only(opening area). no peel off on the other area and it happened on electroless nickel immersion gold finishing only. for other finishing is not affected. kindly advise if you
Electronics Forum | Tue Oct 19 19:25:40 EDT 1999 | Jeff Sanchez
Carol, I think the guys are right about you stand off problem but I want to address the wrinkleing of your masking. Although I think the temps you are subjecting the board to are very high and more than likely creating problems of their own. I th
Electronics Forum | Tue Oct 19 19:44:19 EDT 2010 | laen
I'm looking to mix up a batch of purple solder mask. Has anyone found a good ratio of red and blue that produces a pleasing purple? 50/50 produces a pretty ugly grape color. Is there a standard ratio most fabs use?
Electronics Forum | Tue Dec 10 13:35:34 EST 2019 | scotceltic
I am looking to see what people are using for a min-max range to supply your PCB fabricators regarding solder mask thickness. I saw some points in the archives but not too much regarding what people are providing as their spec ? Any help would be a
Electronics Forum | Wed Jan 05 16:46:44 EST 2000 | Dennis O'Donnell
Several methods work well. 1. (Low Volume Method) Using an Xacto blade, scrape off the solder mask holding the blade flush being careful not to use the pointed part of the blade. 2. (High Volume Method)Tape off the area that you don't want the mas
Electronics Forum | Tue Oct 19 10:53:14 EDT 1999 | Carol Zhang
Hi, I tried to use high temperature solder (540 - 570F)to connect four spacers on the board. The solder mask around the spacers wrinkled a lot.I can even see a few bulbs around it. I use hot plate and solder rings. After hot plate is heated to appr
Electronics Forum | Thu Oct 21 23:20:05 EDT 2010 | camtechpcb
According to the Trichromatism.Half red and half blue will get purple.But the trichromatism only apply to color light. The red and blue soder mask are coloring material.Both of them absorb light.You mixed them up,so you lose blue and red,and get grap